NiAl95/5
INTRODUCTION
Nickel Aluminum 95/5 thermal spray wires can be used as bond coatings and for machine element restoration widely. Pre-alloy suitable for electric arc spraying of nickel-aluminum base material. Dense coating with oxidation, thermal shock and scratch resistance to high temperature performance, combined with strength in 55MPa or more. The coating can also be used directly as a working layer to use.
Equivalent to: Tafa 75B, Oerlikon Metco 8400, PMET885.
CHEMICAL COMPOSITION
composition |
Al % |
Ni% |
---|---|---|
Min |
4.5 |
- |
Max |
- |
Bal |
Deposit Characteristics
Physical Properties:
Grade | Density | Melting Point | Electrical resistivity at 20°C Ω mm2/m |
---|---|---|---|
Nickel Aluminum 95/5 | 8.2g/cm3 | 1430°C | 0.42 |
Typical Deposit Characteristics:
Typical Hardness | Bond Strenghth | Deposit Rate | Deposit Efficiency | Machilityineab |
---|---|---|---|---|
HRB 75 | 9500 psi | 10 lbs/hr/100A | 60-70% | Good |
Diamenter (mm)
1.6,2.0 , 2.3 , 3.17
Production process
Spray process
Arc Spray
Arc spraying is the use of electric arc burning in two consecutive fed between the wires to melt the metal, with a high velocity gas stream molten metal atomization, and the atomization of the sprayed metal particles so that they accelerate the work to form a coating technology .
Flame Spray
The use of a flame as the heat source, the metal and non-heated to a molten state, forming a mist flow in the state of high-speed air jet to the substrate, the injection of the molten minute particles impact upon the substrate above, plastic deformation, into a sheet shape superimposed sedimentary layers.
Application
Backing material used for Arc spray
Suitable for electric arc spraying of nickel-aluminum base material. Dense coating having oxidation, thermal shock and scratch resistance to high temperature performance, combining strength 55MPa or more. The coating can also be used directly as a working layer use.
Backing material used for Flame spray
Nickel aluminum wire is an excellent combination of base material, it plays an important role in the wire flame spraying. In the spraying process, the composite wire between the constituent elements exothermic reaction increases the temperature of the sprayed particles can be "micro-metallurgical" in combination with a variety of metal matrix formation. Dense coating, high temperature, thermal shock. It can be used as aviation, metallurgy, nonferrous metals, transportation, chemical industry all kinds of parts sprayed layer bonding layer. In addition, the nickel-aluminum composite coating itself also has good high temperature oxidation resistance, can be used directly as a working layer.
Packing and shipping
Packaging
Label
Brand, Neutral or Customized
Lead time
According to the quantity
Delivery
Courier:3 - 5 days
Air:5 - 7 days
Sea:30 - 50 days
Please Feel free to give your inquiry in the form below.We will reply you in 24 hours.